Cylinder Head Gasket,Head Gasket Sets & Manifold Gasket Manufacturer

LGP Sealing double perforated metal reinforced with asbestos insert MA001

LGP Sealing Double Perforated Metal Reinforced With Asbestos Insert LGP-MA001
it made by two sides perforated metal with asbestos beater paper insert.
metal usual be 0.2-0.25mm carbon steel,called tinplate,it also can be SS201,304,316.
products feature;
1.Good adaptability and durability,good sealing,no delamination,high yield.
2.An ecological sealing gasket and exhaust,manifold gasket material.
Application:
it suitable for high temperature and high pressure operate environment.mostly they are raw material of exhaust gasket and manifold gasket.
Thickness:1.0-6.0mm
Size:
500 x 500mm;500 x 1000mm;500 x 1500mm;1000 x 1000mm;1000 x 15000mm;
LGP No. LGP-MA001
Compressibility (%,at 34.5 MPa) 8-17% Recovery(%) ≥35%
150℃,At ASTM 3#Oil for 5hours Weight Increase ≤30% Thickness Increase ≤20%
At 21℃~30℃,ASTM B Fuel for 5hours Weight Increase ≤30% Thickness Increase ≤20%

LGP Sealing double perforated metal reinforced with None asbestos insert MA002

LGP Sealing Double Metal Reinforced Gasket with Non Asbestos Insert LGP-MA002
Product Formation:
It made from two sides perforated metal with non asbestos beater paper insert. Metal usual be 0.2-0.25mm carbon steel, called tinplate. It also can be ss201, 304,316.Non asbestos beater sheet is 100% non asbestos.
Product Features:
·Good adaptability and durability, good sealing, no delamination, high yield
·An economical sealing gasket and exhaust, manifold gasket material
·Proved by ISO 9001 UKAS,100% no asbestos
Product Application:
It many suitable for high temperature and high pressure operate environment. Mostly they are raw material of exhaust gasket and manifold gasket
Product Size:
Thickness:1.0-6.0mm Notice: While thicker, it can be 3+2 type(Product section from top to bottom in order are Metal-Paper-Metal-Paper-Metal)
Size:500*500mm;500*1000mm;500*1500mm;1000*1000mm;1000*1500mm
Size can be customized by clients.
LGP No. LGP-MA002
Compressibility 8-17% Recovery ≥35%
150ºC,At ASTM 3#Oil for 5hours Weight Increas ≤30% Thickness Increas ≤20%
At 21ºC~30ºC,ASTM B Fuel for 5hours Weight Increas ≤30% Thickness Increas ≤20%

LGP Sealing Double Metal Reinfoced Exhaust Gasket Sheet with Graphite Insert LGP MA003 1 - MATERIAL

LGP Sealing Double Metal Reinfoced Exhaust Gasket Sheet with Graphite Insert LGP-MA003
Product Formation:
It made from two sides perforated metal with flexible graphite sheet insert. Metal usual be 0.2-0.25mm carbon steel, called tinplate. It also can be ss201, 304,316. Carbon content are 95,97,98,99% for selected.
Product Features:
·Good adaptability and durability, good sealing, no delamination, high yield
·An economical sealing gasket and exhaust, manifold gasket material
·Good oil-resistance, High temperature and high pressure
Product Application:
It many suitable for high temperature and high pressure operate environment. Mostly they are raw material of exhaust gasket and manifold gasket
Product Size:
Thickness:1.0-6.0mm Notice: While thicker, it can be 3+2 type(Product section from top to bottom in order are Metal-Paper-Metal-Paper-Metal)
Size:500*500mm;500*1000mm;500*1500mm;1000*1000mm;1000*1500mm
Size can be customized by clients.
LGP No. LGP-MA003
Compressibility 8-17% Recovery ≥35%
150ºC,At ASTM 3#Oil for 5hours Weight Increas ≤30% Thickness Increas ≤20%
At 21ºC~30ºC,ASTM B Fuel for 5hours Weight Increas ≤30% Thickness Increas ≤20%

LGP Sealing Reinforced Non Asbestos Gasket Sheet with Metal LGP MA004 - MATERIAL

LGP Sealing Reinforced Non Asbestos Gasket Sheet with Metal LGP-MA004
Product Formation:
It made from two sides non asbestos beater sheet with perforated metal insert. Metal usual be 0.2-0.25mm carbon steel, called tinplate. It also can be ss201, 304,316.
Product Features:
·Good adaptability and durability, good sealing, no delamination, high yield
·An economical sealing gasket and exhaust, manifold gasket material
·Good oil-resistance. Notice: Can’t suitable for water
·Proved by ISO9001 UKAS,100% no asbestos
Product Application:
It suitable for oil sealing and gasket, cylinder head gasket
Product Size:
Thickness: 1.0-6.0mm Notice: While thicker, it can be 3+2 type(Product section from top to bottom in order are Paper-Metal-Paper-Metal-Paper) and Multi paper bonding technology
Size: 500*500mm;500*1000mm;500*1500mm;1000*1000mm;1000*1500mm Size can be customized by clients.
Physical Property:
LGP No. LGP-MA004
Compressibility 8-18% Recovery ≥40% Tensile Strength ≥30MPa
150ºC,At IRM903# for 5hours Weight Increase ≤10% Thickness Increase ≤15%
At 21ºC~30ºC,ASTM B Fuel for 5hours Weight Increase ≤10% Thickness Increase ≤15%

LGP Sealing Reinforced Non Asbestos Sheet with Metal Coated Graphite MA005 - MATERIAL

LGP Sealing Reinforced Non Asbestos Sheet with Metal Coated Graphite MA005
Product Formation:
It made from two sides non asbestos beater sheet coated graphite with perforated metal insert. Metal usual be 0.2-0.25mm carbon steel, called tinplate. It also can be ss201, 304,316.
Product Features:
·Good adaptability and durability, good sealing, no delamination, high yield
·An economical sealing gasket and exhaust, manifold gasket material
·Good oil-resistance. Notice: Can’t suitable for water
·Proved by ISO9001 UKAS,100% no asbestos
Product Application:
It suitable for oil sealing and gasket, cylinder head gasket
Thickness: 1.0-6.0mm Notice: While thicker, it can be 3+2 type(Product section from top to bottom in order are Paper-Metal-Paper-Metal-Paper) and Multi paper bonding technology
Size: 500*500mm;500*1000mm;500*1500mm;1000*1000mm;1000*1500mm Size can be customized by clients.
LGP No. LGP-MA005
Compressibility 8-18%
Recovery ≥40%
Tensile Strength ≥30MPa

LGP Sealing Reinforced Flexible Graphite Gasket with Perforated Metal MA006 - MATERIAL

LGP Sealing Reinforced Flexible Graphite Gasket with Perforated Metal MA006
Product Formation:
It made from two sides flexible graphite sheet with perforated metal insert. Metal usual be 0.2-0.25mm carbon steel, called tinplate. It also can be ss201, 304,316. Carbon content are 95,97,98,99% for selected.
Product Features:
·Good adaptability and durability, good sealing, no delamination, high yield
·An economical sealing gasket and exhaust, manifold gasket material
·Good oil-resistance.
·Suitable for High temperature and pressure resistance
Product Application:
It suitable for oil sealing and gasket, cylinder head gasket
Product Size:
Thickness:1.0-6.0mm Notice: While thicker, it can be 3+2 type(Product section from top to bottom in order are Paper-Metal-Paper-Metal-Paper) and Multi paper bonding technology
Size: 500*500mm;500*1000mm;500*1500mm;1000*1000mm;1000*1500mm Size can be customized by clients.
Physical Property:
LGP No. LGP-MA006
Compressibility 8-18%
Recovery ≥40%
Tensile Strength ≥30MPa
150ºC,At IRM903# for 5hours Weight Increase ≤10%
Thickness Increase ≤15%
At 21ºC~30ºC,ASTM B Fuel for 5hours Weight Increase ≤10%
Thickness Increase ≤15%

LGP Sealing Compressed Non Asbestos Gasket Sheet MA007 - MATERIAL

LGP Sealing Compressed Non Asbestos Gasket Sheet MA007
Product Information:
It made of aramid fiber, non asbestos mineral fiber, synthetic fiber, synthetic oil resistant rubber, Compressed by hot roller, vulcanized.
Product Type
It have following type based on different temperature(Numbers means peak temperature)
CSNXB150; CSNXB250; CSNXB350
Product Features:
·Good adaptability and durability, good sealing, no delamination, high yield
·An economical sealing gasket and exhaust, manifold gasket material
·Proved by ISO9001 UKAS,100% no asbestos
·Good oil-resistance.
Product Application:
Engine, Air compressor, Gearbox ,Pipe line and Flange sealing
Thickness: 0.5-5.0mm
Size:1500*1500mm,1500*2000mm,1500*4500mm,1270*1270mm,1270*3810mm can be customized by clients.
Physical Property:
LGP No. LG-MA007A LG-MA007B LG-MA007C
Tensile Strength 7Mpa 8Mpa 10Mpa
Compressibility ’7-17%
Recovery ≥40% ≥45% ≥50%
Creep relaxation ≤40% ≤35% ≤30%
Density 1.8±0.1 g/cm3
Flexibility at room temperature Bend 180°C on the rod with diameter which is 12 times of nominal thickness of the sample, no crack.
Immersed into ASTM 3# at 150ºC for 5h Tensile Strength ≥5MPa ≥5MPa ≥5MPa
Weight Increase ≤30%
Immersed into ASTM B at21-30ºC for 5h Thickness Increase 0-20
Flexibility No crack
Working Temperature Max/Continuous 200/150ºC 300/250ºC 350/300ºC
Working Pressure Max/Continuous 2.0/1.0MPa 4.0/2.0MPa 5.0/3.0MPa

LGP Sealing Non Asbestos Paper Gasket Sheet MA008

LGP Sealing Non Asbestos Paper Gasket Sheet MA008
Product Formation:
It made from latex rubber,asbestos fibre and inorganic filler, adding chemical additives accordingly, it take beater methods.
Product Features:
·Good adaptability and durability, good sealing, no delamination, high yield
·Proved by ISO 9001 UKAS
·Can coated Anti-sticking
·An economical sealing gasket and exhaust, manifold gasket material
·It suitable for make Reinforced or Unreinforced gasket sheet
·Good for use with petrol
Product Application:
It is widely used to make the cylinder head gasket’s materia,engine oil pan gasket,and is used as a sealing gasket material, and is suitable for the special seal of various water,oil mediums
Thickness: 0.5-3.0mm
Size:1100*1200mm
Physical Property:
LGP No. LGP-MA008
Temperature 150-250Deg.
Density 1.45-1.6 g/cm³
Tensile Strength 2.5 Mpa
Compressibility 40±7 ≥%
Compressibility 20 ≥%
Stress Relaxation 30 ≤%
In 150±2ºC,20# Aviation Fuel for 30mi Oil Absorption Rate ≤30%
Thickness Increase  ≤12%
In 15-30ºCWater for 5hours Thickness Increase  ≤12%

  • ADDRESS:NO.333 JIANGBEI DISTRICT,CHONGQING CHINA
  • ZIP:400010
  • +86-23-86886623
  • +86-23-86886332
  • +86-18580150195
  • MANAGER@LGPGASKET.COM
error: Content is protected !!